Pri rabè Pva Solutions - résine klori polyvinyl (PVC) - Yeyuan
Pri rabè Pva Solutions - résine klori polyvinyl (PVC) - Yeyuan Detay:
Polyvinyl lori résine (PVC): poud blan nan aparans. Li se lajman ki itilize nan pwodwi endistriyèl, kwi etaj, kwi atifisyèl, tiyo, fil ak câbles, fim anbalaj, materyèl kimen, elatriye anbalaj la se 25kg / sak, 600kg / sak ak 1200kg / sak.
DG-1300: pwodiksyon materyèl kab, fim fre-kenbe, elatriye.
DG-1000k: pwodiksyon Des plastik, tiyo, elatriye
DG-1000s: pwodiksyon fim anbalaj, elatriye
DG-800: pwodiksyon fèy anbalaj, fèy medikal, elatriye
DG-700: pwodiksyon ekipman tiyo, plak kimen, elatriye
Endikatè prensipal estanda pwodwi (Q / 12 hg5220-2019)
Pwojè | DG-1300 | DG-1000K | DG-1000S | DG-700 | DG-800 |
Mwayèn degre polymérisation P | 1221-1380 | 981-1080 | 981-1080 | 651-750 | 751-850 |
Dansite aparan, g / ml | 0.46-0.54 | 0.51-0.57 | 0.51-0.57 | 0.53-0.61 | 0.54-0.60 |
Whiteness (160 ℃, 10min),% ≥ | 78 | 78 | 78 | 75 | 78 |
Tablo ki koresponn nan degre polymérisation, viskozite ak valè K
Mwayèn degre polymérisation | 2351-2650 | 1221-1380 | 981-1080 | 771-870 | 751-750 | 651-750 | 481-600 | 401-500 |
Viskozite, ml / g | 222-248 | 125-138 | 105-138 | 87-96 | 86-94 | 73-86 | 62-72 | 57-64 |
K valè | 89-93 | 70-73 | 65-67 | 60-62 | 59-62 | 55-59 | 51-55 | 49-51 |
Foto detay pwodwi:
Gid pwodwi ki gen rapò:
Nou ap konsantre tou sou amelyore jesyon bagay la ak sistèm QC pou nou ka kenbe gwo avantaj nan biznis la feròs-konpetitif pou pri rabè Pva Solutions - Polyvinyl chloride résine (PVC) - Yeyuan , Pwodwi a pral bay nan tout mond lan, tankou: Kowet, Miami, Milan, Koulye a, nou pwofesyonèl founi kliyan ak pwodwi prensipal nou yo ak biznis nou an se pa sèlman "achte a" ak "vann", men tou, konsantre sou plis. Nou vize yo dwe founisè rete fidèl ou ak kowoperatè alontèm nan Lachin. Koulye a, nou espere vin zanmi avè ou.
Pa Meroy soti nan Ongri - 2017.11.12 12:31
Li se yon trè bon, trè ra patnè biznis, kap pou pi devan pou pwochen koperasyon an plis pafè!
Pa Martin Tesch soti nan Cape Town - 2018.10.09 19:07